Page 608 - Lewis

Alexseal Yacht Coatings 607
®

®
ALEXSEAL Protective Primer 161
ALEXSEAL ® Protective Primer 161 is a two-component primer based on epoxy resins. Due to specific
corrosion inhibitors and a combination of epoxy resin binding agents, this primer offers excellent adhe-
sion promotion on all substrates as well as corrosion protection on steel and aluminium substrates.
The long re-coating times of ALEXSEAL ® Protective Primer 161 allows an economical appliaction
process. After curing, ALEXSEAL ® Protective Primer 161 is the ideal adhesion promoter for additional
layers of ALEXSEAL ® products. ALEXSEAL ® Protective Primer 161 is used for corrosion protection and
adhesion promotion on steel and aluminium subdtrates, both above and below the waterline.
Mixing Ratio: 6 Parts by Volume P1610/1615 ALEXSEAL ® Protective Primer 161 White/Yellow
1 Part by Volume C1617 ALEXSEAL ® Protective Primer 161 Converter
10% Reduction (vol.) R4042 ALEXSEAL ® Epoxy Primer Reducer
Allow a 15 minute induction period after mixing base and converter, add reducer and remix.
Example: 6 : 1 : 1/2 = 7% reduction.

Application: Viscosity Zahn #2: approx. 80 sec., DIN 4 cup 4 mm: approx. 70 sec.
Fluid Nozzle Size 1.4 to 1.6 mm (0.55 to 0.60) – Conventional & HVLP
Atomizing Pressure 3.0 to 5.0 bar (42 to 70 PSI) – Conventional & HVLP
Pot Pressure 0.7 to 1.5 bar (10 to 20 PSI) – Conventional & HVLP
Airless Equipment Tip 0.35 mm - 60 to 0.43 mm – 60 (0.014-60 to 0.017-60)
Airless Equipment Pressure 3.0 to 5.0 bar (42 to 70 PSI)
Apply 1-2 coats to a total wet film thickness (WFT) of 200-225 microns (8-9mils).
This will achieve a dry film thickness (DFT) of 75-125 microns (3-5 mils).
Technical Data Sheet and MSDS Sheets available on request or visit www.alexseal.com
FIG 1ALX

No. Each Size Description
P1610G $212.00 Gallon White 161 Protective Primer
P1615G 212.00 Gallon Yellow 161 Protective Primer
C1617P 70.00 Pint 161 Primer Converter

ALEXSEAL Cor Spec Primer 135 WHILE ALEXSEAL ®
®
SUPPLIES
LAST

ALEXSEAL ® Cor Spec Primer 135 is a chromate containing, two component epoxy primer for use
on metal substrates. This product is highly resistant to corrosion and chemicals. ALEXSEAL ® Cor
Spec Primer 135 is designed to prime and seal old and new, property prepared, metal surfaces
prior to the application of ALEXSEAL ® Topcoats or ALEXSEAL ® Finish and Surfacing Primers.
This product is ideal for masts, parts and metal substrates. It may be top coated directly or
primed depending on the application requirements. Cor Spec Primer 135 may be used above and
below the waterline. YACHT COATINGS

Mixing Ratio: 3 Parts by Volume P1352 ALEXSEAL ® Cor Spec 135 Base
1 Part by Volume C1357 ALEXSEAL ® Cor Spec 135 Converter
Allow a 15 minute induction period after mixing base and converter.
Example: 3 : 1 no reduction for spray or brush application.

Application: Viscosity (Zahn #2) Approx. 15 sec.
Fluid Nozzle Size Pressure Pot 1.0 to 1.2 mm (0.040 to 0.046) – Conventional & HVLP
Fluid Nozzle Size Siphon Cup 1.6 mm (0.070) – Conventional & HVLP
Atomizing Pressure 3.0 to 5.0 bar (42 to 70 PSI) – Conventional & HVLP
Pot Pressure 0.7 to 1.5 bar (10 to 15 PSI) – Conventional & HVLP
Airless Equipment Tip 0.22 mm- (0.009) to 0.012- (0.3 mm) – 50-65° fan
Airless Equipment Pressure 2 to 4 bar (30 to 56 PSI)

Apply one coat to a total wet film thickness (WFT) of 40-50 microns (1.7 - 2.0 mil).
This will achieve a dry film thickness (DFT) of 25 microns (1 mil). Minimum recommended film is 25
microns (1 mil) DFT. Maximum recommended film thickness during a spray application is 1 coat,
totalling 50 microns (2.0 mil) WFT, or 25 microns (1 mil) DFT.
Technical Data Sheets and MSDS Sheets available on request or visit www.alexseal.com

FIG 1ALX

No. Each Size Description
P1352 $150.00 3/4 Gallon Cor Spec Primer 135 (Mix Ratio: 3:1)